high alumina cement

High temperature high alumina cement 1). High strength under high temperature 2).As bonded agent of confecting catable

High temperature resisting high alumina cement

1. Features: 1). High strength under high temperature2).As bonded agent of confecting catable

2.Quality:

 high alumina Cement manufactured by sintered method in rotary kiln are according with up-to-date standard GB201-2000,which are graded as G6,G7.Other new products super-early-strength type CA50-N and high-strength type CA50-G9 are to be introduced in addition,whose quality standard are based on CA50 OF GB201-2000.

3.Properties:

Model No.:		HXCA-50-G6
Chemical composition
Al2O3SiO2Fe2O3R2OSCl	%	above 50,below 60below 8.0below 2.5below 0.4
Physical properties
fineness
0.045 residue	%
Blaine	m2/kg	above 300
Setting time
initial	h:min	above 30
final		below 6
Flexural strength
6h	MPa
1d		6.0
3d		7.0
Compressive strength
6h	MPa
1d		45
3d		55

4.Application:

Therefore it is suitable to make refractory concrete as a binder. Depending on the refractory aggregates (fireclay, high alumina)which are used, the refractory concrete made of the cement can be used below 1400 centigrade.If it is used in construction, attention given in the appendix GB201 must be followed.

5.Testingmethod                                                                                                                                                                                                                               Chemical: Composition: According with GB/T205.  Blaine: According GB/T8074.  Fineness: According with GB/T1345 with screen of 0.045mm.  Setting time: According with the addenda A of GB/TGB201-2000.  Strength: According with the amendment prescribe of GB/T1767 and GB201-2000.6.Packing Adopted specified by GB9774 cement packing sack,25kg or 50kg in PE bag with a complex bag of woven plastic and kraft paper outside.

 7.Note Keep in dry conditions and prevent humidity during storage and transportation. Don't mix with other variety of cements.

high alumina cement